牌號
|
S51770不銹彈簧鋼絲
|
|
|
|
|
|
|
|
|
中國ISC
|
07Cr17Ni7Al
|
|
|
|
|
|
|
|
|
舊牌號
|
0Cr17Ni7Al
|
|
|
|
|
|
|
|
|
對應(yīng)標(biāo)準(zhǔn)
|
GB /T 24588-2019
|
|
|
|
|
|
|
|
|
不銹彈簧鋼絲
|
|
|
|
|
|
|
|
|
en:Stainless steel wires for spring
|
|
|
|
|
|
|
|
|
歸類
|
沉淀硬化型不銹鋼
|
|
|
|
|
|
|
|
|
性能
|
彈性 耐腐蝕
|
|
|
|
|
|
|
|
|
標(biāo)簽
|
沉淀硬化型不銹鋼
|
|
|
|
|
|
|
|
|
說明
|
本標(biāo)準(zhǔn)適用于制作彈簧用奧氏體型和沉淀硬化型不銹彈簧鋼絲
|
|
|
|
|
|
|
|
|
密度
|
7.93 g/cm3
|
|
|
|
|
|
|
|
|
07Cr17Ni7Al 化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Al
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
16
|
6.5
|
0.75
|
|
ZUI DA值
|
0.09
|
1
|
1
|
0.04
|
0.03
|
18
|
7.75
|
1.5
|
|
|
|
|
|
|
|
|
|
|
|
07Cr17Ni7Al 機(jī)械性能
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態(tài)
|
抗拉強(qiáng)度
|
|
|
|
|
|
|
|
σb
|
|
|
|
|
|
|
|
Mpa
|
|
|
|
|
|
|
|
冷拉鋼絲；d<0.2
|
|
C組
|
|
|
|
|
|
|
|
≥1970
|
|
|
|
|
|
|
|
冷拉鋼絲；0.2≤d<0.3
|
|
≥1950
|
|
|
|
|
|
|
|
冷拉鋼絲；0.3≤d<0.4
|
|
≥1920
|
|
|
|
|
|
|
|
冷拉鋼絲；0.4≤d<0.5
|
|
≥1900
|
|
|
|
|
|
|
|
冷拉鋼絲；0.5≤d<0.63
|
|
≥1850
|
|
|
|
|
|
|
|
冷拉鋼絲；0.63≤d<0.8
|
|
≥1820
|
|
|
|
|
|
|
|
冷拉鋼絲；0.8≤d<1
|
|
≥1800
|
|
|
|
|
|
|
|
冷拉鋼絲；1≤d<1.2
|
|
≥1750
|
|
|
|
|
|
|
|
冷拉鋼絲；1.2≤d<1.5
|
|
≥1700
|
|
|
|
|
|
|
|
冷拉鋼絲；1.5≤d<1.6
|
|
≥1650
|
|
|
|
|
|
|
|
冷拉鋼絲；1.6≤d<2
|
|
≥1600
|
|
|
|
|
|
|
|
冷拉鋼絲；2≤d<2.5
|
|
≥1550
|
|
|
|
|
|
|
|
冷拉鋼絲；2.5≤d<3
|
|
≥1500
|
|
|
|
|
|
|
|
冷拉鋼絲；3≤d<3.5
|
|
≥1450
|
|
|
|
|
|
|
|
冷拉鋼絲；3.5≤d<4
|
|
≥1400
|
|
|
|
|
|
|
|
冷拉鋼絲；4≤d<4.5
|
|
≥1350
|
|
|
|
|
|
|
|
冷拉鋼絲；5≤d<6
|
|
≥1300
|
|
|
|
|
|
|
|
冷拉鋼絲；6≤d<7
|
|
≥1250
|
|
|
|
|
|
|
|
冷拉鋼絲；7≤d<8
|
|
≥1200
|
|
|
|
|
|
|
|
冷拉鋼絲；8≤d<10
|
|
≥1150
|
|
|
|
|
|
|
|
試樣；d<0.2
|
時(shí)效
|
2270~2610
|
|
|
|
|
|
|
|
試樣；0.2≤d<0.3
|
時(shí)效
|
2250~2580
|
|
|
|
|
|
|
|
試樣；0.3≤d<0.4
|
時(shí)效
|
2220~2550
|
|
|
|
|
|
|
|
試樣；0.4≤d<0.5
|
時(shí)效
|
2200~2530
|
|
|
|
|
|
|
|
試樣；0.5≤d<0.63
|
時(shí)效
|
2150~2470
|
|
|
|
|
|
|
|
試樣；0.63≤d<0.8
|
時(shí)效
|
2120~2440
|
|
|
|
|
|
|
|
試樣；0.8≤d<1
|
時(shí)效
|
2100~2410
|
|
|
|
|
|
|
|
試樣；1≤d<1.2
|
時(shí)效
|
2050~2350
|
|
|
|
|
|
|
|
試樣；1.2≤d<1.5
|
時(shí)效
|
2000~2300
|
|
|
|
|
|
|
|
試樣；1.5≤d<1.6
|
時(shí)效
|
1950~2240
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|