牌號(hào)
|
Type 316不銹鋼絲
|
|
|
|
|
|
|
|
|
|
美國(guó)UNS
|
S31600
|
|
|
|
|
|
|
|
|
|
對(duì)應(yīng)標(biāo)準(zhǔn)
|
ASTM A580/A580M-2018
|
|
|
|
|
|
|
|
|
|
不銹鋼絲
|
|
|
|
|
|
|
|
|
|
Stainless Steel Wire
|
|
|
|
|
|
|
|
|
|
歸類(lèi)
|
奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
|
Type 316 化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
N
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
16
|
10
|
2
|
-
|
|
最DA值
|
0.08
|
1
|
2
|
0.045
|
0.03
|
18
|
14
|
3
|
0.1
|
|
|
|
|
|
|
|
|
|
|
|
|
Type 316 機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態(tài)
|
抗拉強(qiáng)度
|
屈服點(diǎn)
|
延伸率
|
斷面收縮率
|
|
|
|
|
|
σb
|
σs
|
δ
|
ψ
|
|
|
|
|
|
Mpa
|
Mpa
|
%
|
%
|
|
|
|
|
|
A
|
冷精軋
|
≥620
|
≥310
|
≥30
|
≥40
|
|
|
|
|
|
A
|
退火
|
≥520
|
≥210
|
≥35
|
≥50
|
|
|
|
|
|
注:Condition A —— Annealed as a final heat treatment.
|
|
|
|
|
|
|
|
|
|
|
Material in Condition A may be given a final cold drawing for size control or finish, or both, slightly raising tensile strength.
|
|
|
|
|
|
|
|
|
|
|