PA66 71G33L 美國杜邦公司 物性數(shù)據(jù)
|
②原料技術(shù)數(shù)據(jù)
|
性能項目
|
試驗條件[狀態(tài)]
|
測試方法
|
測試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
基本性能
|
吸水率
|
24小時浸漬(23℃)
|
ASTM D-570
|
0.5
|
%
|
|
吸水率
|
飽和(23℃)
|
ASTM D-570
|
4.6
|
%
|
|
物理性能
|
比重
|
---
|
ASTM D-792
|
1.35
|
---
|
|
機械性能
|
洛氏硬度M
|
DAM
|
ASTM D-785
|
M96
|
---
|
|
洛氏硬度M
|
50%RH
|
ASTM D-785
|
M90
|
---
|
|
洛氏硬度R
|
DAM
|
ASTM D-785
|
R122
|
---
|
|
洛氏硬度R
|
50%RH
|
ASTM D-785
|
R118
|
---
|
|
泰伯磨耗量
|
50%RH
|
---
|
36
|
cycles
|
|
拉伸強度
|
23℃,DAM
|
ASTM D-638
|
151.6
|
MPa
|
|
拉伸強度
|
23℃,50%RH
|
ASTM D-638
|
110.3
|
MPa
|
|
斷裂伸長率
|
23℃,DAM
|
ASTM D-638
|
3
|
%
|
|
斷裂伸長率
|
23℃,50%RH
|
ASTM D-638
|
4
|
%
|
|
擠剪強度
|
23℃,DAM
|
ASTM D-732
|
72
|
MPa
|
|
撓曲模量
|
23℃,DAM
|
ASTM D-790
|
6895
|
MPa
|
|
撓曲模量
|
23℃,50%RH
|
ASTM D-790
|
5516
|
MPa
|
|
撓曲強度
|
23℃,DAM
|
ASTM D-790
|
228
|
MPa
|
|
埃佐沖擊強度
|
23℃,DAM
|
ASTM D-256
|
128
|
j/m
|
|
埃佐沖擊強度
|
23℃,50%RH
|
ASTM D-256
|
128
|
j/m
|
|
電氣性能
|
介電強度
|
DAM
|
ASTM D-149
|
630
|
volts/mil
|
|
介電強度
|
100%RH
|
ASTM D-149
|
255
|
volts/mil
|
|
體積電阻率
|
100%RH
|
ASTM D-257
|
109
|
ohm-cm
|
|
損耗因數(shù)
|
DAM@106Hz赫
|
ASTM D-150
|
0.02
|
---
|
|
體積電阻率
|
DAM
|
ASTM D-257
|
1014
|
ohm-cm
|
|
介電強度
|
(分步法)DAM
|
ASTM D-149
|
510
|
volts/mil
|
|
介電常數(shù)
|
DAM@103Hz赫
|
ASTM D-150
|
4.2
|
---
|
|
介電常數(shù)
|
DAM@106Hz赫
|
ASTM D-150
|
3.4
|
---
|
|
損耗因數(shù)
|
DAM@103Hz赫
|
ASTM D-150
|
0.02
|
---
|
|
熱 性 能
|
熔點
|
50%RH
|
ASTM D-789
|
255
|
℃
|
|
線性熱膨脹系數(shù)
|
---
|
ASTM D-696
|
1.8×10-5
|
m/m/℃
|
|
熔點
|
DAM
|
ASTM D-789
|
255
|
℃
|
|
熱畸變溫度
|
1.8MPa
|
ASTM D-648
|
246
|
℃
|
|