LEXAN?
164R resin
聚碳酸酯
產(chǎn)品說(shuō)明:
Medium viscosity, multi purpose polycarbonate resin with added release
agent. FDA food contact compliant in limited colors.Effective January 15th, 2007
this grade will no longer be supported with biocompatibility information and
should not be used for medical applications which require biocompatibility.
Alternative grade HP4REU.
|
材料狀態(tài)
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區(qū)
|
|
|
添加劑
|
|
|
特性
|
|
|
機(jī)構(gòu)評(píng)級(jí)
|
|
|
RoHS 合規(guī)性
|
|
|
外觀
|
|
|
加工方法
|
|
|
密度
|
1.20
|
g/cm?
|
ISO
1183
|
|
溶化體積流率（MVR） (300°C/1.2
kg)
|
9.50
|
cm?/10min
|
ISO
1133
|
|
收縮率 - 流動(dòng) 3
|
0.50 到 0.70
|
%
|
內(nèi)部方法
|
|
吸水率
|
|
|
ISO
62
|
|
飽和,
23°C
|
0.35
|
%
|
|
|
平衡, 23°C,
50% RH
|
0.15
|
%
|
|
|
球壓硬度 (H 358/30)
|
95.0
|
MPa
|
ISO
2039-1
|
|
拉伸模量
|
2350
|
MPa
|
ISO
527-2/1
|
|
拉伸應(yīng)力
|
|
|
ISO
527-2/50
|
|
屈服
|
63.0
|
MPa
|
|
|
斷裂
|
70.0
|
MPa
|
|
|
拉伸應(yīng)變
|
|
|
ISO
527-2/50
|
|
屈服
|
6.0
|
%
|
|
|
斷裂
|
120
|
%
|
|
|
彎曲模量 4
|
2300
|
MPa
|
ISO
178
|
|
彎曲應(yīng)力 4, 5
|
90.0
|
MPa
|
ISO
178
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17
轉(zhuǎn)輪)
|
10.0
|
mg
|
內(nèi)部方法
|
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度
|
|
|
|
|
-30°C 6
|
14
|
kJ/m?
|
ISO
179/1eA
|
|
23°C 6
|
73
|
kJ/m?
|
ISO
179/1eA
|
|
23°C
|
35
|
kJ/m?
|
ISO
179/2C
|
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 6
|
|
|
ISO
179/1eU
|
|
-30°C
|
無(wú)斷裂
|
|
|
|
23°C
|
無(wú)斷裂
|
|
|
|
懸壁梁缺口沖擊強(qiáng)度 7
|
|
|
ISO
180/1A
|
|
-30°C
|
12
|
kJ/m?
|
|
|
23°C
|
70
|
kJ/m?
|
|
|
無(wú)缺口伊佐德沖擊強(qiáng)度 7
|
|
|
ISO
180/1U
|
|
-30°C
|
無(wú)斷裂
|
|
|
|
23°C
|
無(wú)斷裂
|
|
|
|
熱變形溫度 8
|
|
|
|
|
0.45 MPa,
未退火, 100 mm 跨距
|
138
|
°C
|
ISO
75-2/Be
|
|
1.8 MPa,
未退火, 100 mm 跨距
|
127
|
°C
|
ISO
75-2/Ae
|
|
維卡軟化溫度
|
|
|
|
|
--
|
143
|
°C
|
ISO
306/B50
|
|
--
|
145
|
°C
|
ISO
306/B120
|
|
Ball Pressure Test
|
|
|
IEC
60695-10-2
|
|
125°C
|
Pass
|
|
|
|
140°C 9
|
Pass
|
|
|
|
線形熱膨脹系數(shù) - 流動(dòng) (23 到 80°C)
|
7.0E-5
|
cm/cm/°C
|
ISO
11359-2
|
|
導(dǎo)熱系數(shù)
|
0.20
|
W/m/K
|
ISO
8302
|
|
RTI Elec
|
130
|
°C
|
UL
746
|
|
RTI Imp
|
125
|
°C
|
UL
746
|
|
RTI
|
125
|
°C
|
UL
746
|
|
表面電阻率
|
> 1.0E+15
|
ohm
|
IEC
60093
|
|
體積電阻率
|
> 1.0E+15
|
ohm·cm
|
IEC
60093
|
|
介電強(qiáng)度 (3.20 mm,
在油中)
|
17
|
kV/mm
|
IEC
60243-1
|
|
相對(duì)電容率
|
|
|
IEC
60250
|
|
50
Hz
|
2.70
|
|
|
|
60
Hz
|
2.70
|
|
|
|
1
MHz
|
2.70
|
|
|
|
耗散因數(shù)
|
|
|
IEC
60250
|
|
50
Hz
|
1.0E-3
|
|
|
|
60
Hz
|
1.0E-3
|
|
|
|
1
MHz
|
0.010
|
|
|
|
UL 阻燃等級(jí)
|
|
|
UL
94
|
|
1.50
mm
|
HB
|
|
|
|
3.00
mm
|
HB
|
|
|
|
灼熱絲易燃指數(shù) (1.00 mm)
|
850
|
°C
|
IEC
60695-2-12
|
|
極限氧指數(shù)
|
25
|
%
|
ISO
4589-2
|
|
折射率
|
1.586
|
|
ISO
489
|
|
透射率 (2540 ?m)
|
88.0 到 90.0
|
%
|
ASTM
D1003
|
|
霧度 (2540
?m)
|
< 0.80
|
%
|
ASTM
D1003
|
|
干燥溫度
|
120
|
°C
|
|
|
干燥時(shí)間
|
2.0 到 4.0
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
料斗溫度
|
60.0 到 80.0
|
°C
|
|
|
料筒后部溫度
|
260 到 280
|
°C
|
|
|
料筒中部溫度
|
270 到 290
|
°C
|
|
|
料筒前部溫度
|
280 到 310
|
°C
|
|
|
射嘴溫度
|
270 到 290
|
°C
|
|
|
加工（熔體）溫度
|
280 到 310
|
°C
|
|
|
模具溫度
|
80.0 到 110
|
°C
|
|